Early Age Strength and Heat of Hydration Properties of Concrete containing Silica Fume and Metakaolin

Khawaja Adeel Tariq, Sajid Mehmood, Muhammad Haroon, Ahmad Raza

Abstract


This research work is related to heat of hydration and mechanical properties of the concrete containing silica fume and metakaolin. Total five mixes of concrete were prepared with varying percentages of metakaolin and silica fume. The heat of hydration, tensile strength, compressive strength and flexural strength of concrete that contain silica fume and metakaolin were determined by testing cylinders, beams and cubes. There was replacement of silica fume and metakaolin as 10% and 0-15% respectively in all mixes except control mix. The rise of temperature due to heat of hydration in concrete was calculated by using semi adiabatic approach. The strength of concrete with silica fume and metakaolin increases with curing age as compared to control mix. It was observed that when quantity of metakaolin is increased from 0-10% in silica fume concrete, the temperature rise of concrete was reduced. It was also perceived that further increase in metakaolin i.e. 15% in silica fume concrete results in reduction of strength. Therefore, it can be inferred for the study that silica fume concrete with metakaolin can be used in colder areas where early age strength is required and in mass concrete construction where lower temperature is needed.


Full Text:

PDF

References


Mehta, K.P. (2001). Reducing the environmental impact of concrete, Concrete International, 23(10), 61-66.

Wang, J., & Yan, P. (2013). Evaluation of early age mechanical properties of concrete in real structure. Computers and Concrete, 12(1), 53-64. doi:10.12989/cac.2013.12.1.053.

Ding, J., & Li, Z. (2002). Effects of metakaolin and silica fume on properties of concrete. ACI Materials Journal, 99(4), 393-398.

Brooks, J.J., & Johari, M. M. (2001). Effect of metakaolin on creep and shrinkage of concrete. Cement and Concrete Composites, 23(6), 495-502. doi:10.1016/S0958-9465(00)00095-0.

Kadri, E., Kenai, S., Karim, E., Siddique, R., & Schutter, G. (2011). Influence of metakaolin and silica fume on the heat of hydration and compressive strength development of mortar. Applied Clay Science, 53(4), 704-708. doi:10.1016/j.clay.2011.06.008.

Poon, C.S., Kou, S.C., & Lam, L. (2006). Compressive strength, chloride diffusivity and pore structure of high performance metakaolin and silica fume concrete. Construction and Building Materials, 20(10), 858-65. doi:10.1016/j.conbuildmat.2005.07.001.

Elaty, M.A.A. (2014). Compressive strength prediction of portland cement Concrete with age using a new model. HBRC Journal, 145-155. doi:10.1016/j.hbrcj.2013.09.005.

Dinakar, P., Sahoo, P.K., & Sriram, G. (2013). Effect of metakaolin content on the properties of high strength concrete. International Journal of Concrete Structures and Materials, 7(3), 215-223.

Langan, B.W., Weng, K.., & Ward, M.A. (2002). Effect of silica fume and fly ash on heat of hydration of portland cement. Cement and Concrete Research, 32(7), 1045-1051. doi:10.1016/S0008-8846(02)00742-1.

www.pagelpakistan.com/Pagel. 2019, accessed around 10/4/2019 at 1200PST.

ASTM, C39/C39M-15a (2012). Standard test method for compressive strength of cylindrical concrete specimens. ASTM International.

ASTM, C496 (2006). Standard test method for splitting tensile strength of cylindrical concrete specimens. ASTM International.

ASTM, C78 (2002). Standard test method for flexural strength of concrete (Using Simple Beam with Third-Point Loading). ASTM International.

Alhozaimy, A., Fares, G., Alawad, O.A., & Al-Negheimish, A. (2015). Heat of hydration of concrete containing powdered scoria rock as a natural pozzolanic material. Construction and Building Materials, 81, 113-119. doi:10.1016/j.conbuildmat.2015.02.011.

ASTM, C143 (2015). Standard test method for slump of hydraulic-cement concrete. ASTM International.






Copyright (c) 2020 Pakistan Journal of Engineering and Applied Sciences

Powered By KICS